http://ciateq.repositorioinstitucional.mx/jspui/handle/1020/610| Failure analysis of conformal cooling inserts fabricated by additive manufacturing | |
| Hiram Flores Ruiz Raúl Pérez Bustamante | |
| Acceso Abierto | |
| Atribución-NoComercial-CompartirIgual | |
| https://doi.org/10.1017/S1431927622010625 https://www.cambridge.org/core/journals/microscopy-and-microanalysis/article/failure-analysis-of-conformal-cooling-inserts-fabricated-by-additive-manufacturing/245A97C99DAEAFF7281147191E7D39B5 https://www.cambridge.org/core/journals/microscopy-and-microanalysis | |
| In this work, were analyzed two different conformal cooling inserts fabricated by additive manufacturing in Maraging® steel. The inserts were provided by different suppliers and employed in a 3500 ton HPDC machine. The respective study was carried out after failure of the inserts, which occur after 4000 (insert A) and 8000 (insert B) shots respectively. Scanning electron microscopy (SEM) observations were performed on four and five zones on the fracture area of each insert respectively. Microstructural observations by optical microscopy from the fracture sections were carried out. The mechanical behavior of the samples was evaluated tensile test at room temperature and Charpy tests at three different temperatures. | |
| Microscopy Society of America | |
| 2022 | |
| Artículo | |
| Microscopy and Microanalysis, vol. 28, Supplement S1, p. 2818-2820 | |
| Inglés | |
| Público en general | |
| Flores-Ruiz, H., & Pérez-Bustamante, R. (2022). Failure analysis of conformal cooling inserts fabricated by additive manufacturing. Microscopy and Microanalysis, 28(S1), 2818-2820. https://doi.org/10.1017/S1431927622010625 | |
| OTRAS | |
| Versión publicada | |
| publishedVersion - Versión publicada | |
| Aparece en las colecciones: | Artículos Publicados en Revistas Indexadas |
Cargar archivos:
| Fichero | Tamaño | Formato | |
|---|---|---|---|
| Failure analysis of conformal cooling inserts fabricated.pdf | 624.88 kB | Adobe PDF | Visualizar/Abrir |