http://ciateq.repositorioinstitucional.mx/jspui/handle/1020/631| Evaluación de procesos de aplicación de segunda capa para mejorar la resistencia al tallado de un recubrimiento polimérico base agua aplicado a sustratos vítricos Evaluation of second layer application processes to improve the scratch resistance of a water-based polymeric coating applied to vitric substrates | |
| Elena Hernández Velázquez Daniel Gustavo Martínez Toto María Guadalupe Navarro Rojero | |
| Acceso Abierto | |
| Atribución-NoComercial-CompartirIgual | |
| 2594-1925 https://doi.org/10.37636/recit.v54339362 https://recit.uabc.mx/index.php/revista/article/view/235 https://recit.uabc.mx/index.php/revista/index | |
| Recubrimientos anti-rayado Ácido oleico Silano Deposición química de vapor por combustión (CCVD) Recubrimiento de curado UV Anti-scratch coating Oleic acid Silane Combustion chemical vapor deposition (CCVD) UV curable coating | |
| Tres tipos de recubrimientos fueron evaluados como medio de protección al tallado de un polímero base agua aplicado sobre una superficie vítrica. Las opciones fueron ácido oleico aplicado en fase vapor (AP5), Silano utilizando la técnica de Deposición Química de Vapor por Combustión (CCVD) y un Barniz epóxico de secado UV. Una vez aplicados, cada uno de estos materiales sobre el barniz base agua, fueron puestos en contacto con dos tipos de cartones, poli laminado y laminado a través del método de prueba Rub Tester con el equipo Sutherland 2000TM evaluando el nivel de desgaste para cada caso. Cada uno de los recubrimientos fue caracterizado antes y después de la abrasión, determinando propiedades de brillo, dureza, tensión superficial, transmitancia y lubricidad con el objetivo de conocer el nivel de efectividad de la protección al tallado de la primera capa. Los resultados muestran la mejor protección al tallado aplicando ácido oleico como segunda capa además de tener la ventaja de no afectar las propiedades estéticas del recubrimiento polimérico previo. Tree kinds of anti-scratch coatings were applied to protect a polymer water base applied on a glass surface. Oleic acid (AP5), silane by Combustion Chemical Vapor Deposition (CCVD), and lacquer by curing UV were evaluated. Each one was put in contact with two types of cardboard, laminated and poly laminated using Rub Tester Sutherland 2000TM equipment. At the end of the test, was evaluated the damage level for each sample. The coatings were evaluated both before and after applying the abrasion. Brightness, hardness, superficial tension, transmittance, and lubricity were measured in each case searching the performance level of scratch resistance and protection of the previous film. Results show that the best behavior is reached with oleic acid used as a lubricant. Also, the aesthetic properties of the first coating are not affected. | |
| Universidad Autónoma de Baja California | |
| 2022 | |
| Artículo | |
| Revista de Ciencias Tecnológicas (RECIT), vol. 5, no. 4 (octubre-diciembre), pág. 339-362 | |
| Español | |
| Público en general | |
| Velázquez, E. H., Toto, D. G. M., & Rojero, M. G. N. (2022). Evaluación de procesos de aplicación de segunda capa para mejorar la resistencia al tallado de un recubrimiento polimérico base agua aplicado a sustratos vítricos. REVISTA DE CIENCIAS TECNOLÓGICAS, 5(4), 339-362. https://doi.org/10.37636/recit.v54339362 | |
| OTRAS | |
| Versión publicada | |
| publishedVersion - Versión publicada | |
| Aparece en las colecciones: | Artículos Publicados en Revistas Arbitradas |
Cargar archivos:
| Fichero | Tamaño | Formato | |
|---|---|---|---|
| Evaluacion de procesos de aplicacion.pdf | 690.24 kB | Adobe PDF | Visualizar/Abrir |